PC/ABS合金材料
一、PC/ABS合金材料概述
POLYTOP®鼎塑塑料合金材料PC/ABS不仅具备PC 的超高耐冲击性能和极佳的疲劳性能,亦具有ABS树脂的易成型性,所以应用在薄壁及复杂形状制品时不仅能保持极其优异的综合性能且易成型。
项 目Items |
单 位Units |
测 试 方 法Test Method |
结 果Result |
比 重 Density |
g/cm3 |
ASTM D-792 |
1.15 |
洛氏硬度 Rockwell |
R |
ASTM D-785 |
110 |
拉伸强度 Tensile Strength |
Mpa |
ASTM D-638 |
60 |
弯曲强度 Flexural Strength |
Mpa |
ASTM D-790 |
90 |
弯曲模量 Flexural Modulus |
Mpa |
ASTM D-790 |
2300 |
埃卓冲击强度(有缺口)Izod Impact Strength(notched) |
Kg/cm2 |
ASTM D-256 |
65 |
热变形温度(1.82MPa)Heat Distortion Temp |
℃ |
ASTM D-648 |
108 |
模塑收缩率 Molding Shrinkage |
% |
ASTM D-955 |
0.5-0.7 |
熔融指数 Melt Flow Index |
g/10 min |
ASTM D-1238 |
15 |
阻燃等级 Flammability |
-- |
UL 94 |
HB |